Product Details:
|
Use:: | Spinning | Fineness:: | 0.5D To 25D |
---|---|---|---|
Raw Material:: | 100% Polyester Chip | Color:: | Brite Raw White |
Fiber Length:: | 32mm/38mm/51mm/65mm/76mm/102mm | Fiber Type:: | Staple |
High Light: | 38mm polyester yarn raw material,SGS flame resistant fibers,1.5dtex polyester raw material |
Bright Raw White 1.5dtex×38mm Polyester Raw Material For Making Glove Yarn
---Bright Raw White 1.5dtex×38mm
---Good Tenacity , Low Defects
NO. |
ITEM |
UNIT |
ANALYSIS RESULT |
Testing standard |
||||||
1 |
Breaking tenacity |
cN/dtex |
6.27 |
GB/T14337 |
||||||
2 |
Elongation at break rate |
% |
20.5 |
GB/T14337 |
||||||
3 |
Linear density deviation rate |
% |
0.8 |
GB/T14335 |
||||||
4 |
Length deviation rate |
% |
0.8 |
GB/T14336 |
||||||
5 |
Double-length textile fiber content |
mg/100g |
0.4 |
GB/T14336 |
||||||
6 |
Defects content |
mg/100g |
0.7 |
GB/T14339 |
||||||
7 |
Crimp number |
each/25mm |
12.5 |
GB/T14338 |
||||||
8 |
Crimp rate |
% |
11.2 |
GB/T14338 |
||||||
9 |
Dry and heat shrinkage rate to 180℃ |
% |
4.7 |
FZ/T50004 |
||||||
10 |
Strength of 10% constant elongation |
cN/dtex |
4.46 |
GB/T14337 |
||||||
11 |
Specific resistance |
Ω·cm |
2.1×107 |
GB/T14342 |
||||||
12 |
Coefficient of variation breaking tenacity |
% |
6.10 |
GB/T14337 |
||||||
13 |
deviation coefficient of elongation |
% |
20.2 |
GB/T14337 |
||||||
14 |
moisture regain |
% |
0.5 |
GB/T6503 |
||||||
15 |
oil content |
% |
0.19 |
GB/T6504 |
||||||
16 |
linear density |
dtex |
1.34 |
GB/T14335 |
||||||
17 |
LA=length average |
mm |
38.3 |
GB/T14336 |
Recycled:
Luster: SD RW, SD BLK, SSW, TBR RW, DD
Length: 24mm - 108mm
Denier: 1.5D – 15D
Luster: SD RW, SD OB, BR RW, BR OB
Length: 26mm – 76mm
For Spinning: 0.9D – 1.5D
For Non-Woven: 1.4D – 6D
Suzhou Henghao Import And Export Co.,ltd
CHEMICAL PRODUCT---POLYESTER STAPLE FIBER; TOPS,PE/PP
SPARE PARTS FOR WEAVING AND SPINNING
wish have the chance to cooperate with good of u
Contact Person: Mr. James
Tel: 86-13915553949